T (°C) | Solution | Ecorr(mV vs. SCE) | Icorr(mAcm−2) | βc(mV/dec) | βa(mV/dec) | θ | η(%) |
---|---|---|---|---|---|---|---|
25 | Blank | −482 | 0.606 | 102 | 101 | 0.22 | 22% |
Copolymer | −46 | 0.469 | 101 | 50 | |||
30 | Blank | −471 | 1.399 | 136 | 100 | 0.42 | 42% |
Copolymer | −467 | 0.793 | 104 | 54 | |||
40 | Blank | −468 | 4.279 | 141 | 106 | 0.70 | 70% |
Copolymer | −480 | 1.260 | 117 | 78 | |||
50 | Blank | −471 | 8.519 | 161 | 129 | 0.50 | 50% |
Copolymer | −469 | 4.187 | 134 | 83 |