Table 12 Chemical composition of E500 and F500W weld metal
From: Evaluation of applicability of thick E500 TMCP and F500W QT steel plates for Arctic service
Steel grade and plate thickness | Welding process | Amount of alloying elements in the weld, wt. % | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|
C | Si | Mn | Ni | Cr | Cu | Mo | S | P | ||
E500, 25 mm | MMA | 0.07 | 0.37 | 1.92 | 2.32 | 0.29 | 0.10 | 0.27 | 0.012 | 0.013 |
FCAW | 0.06 | 0.41 | 1.66 | 2.57 | 0.06 | – | – | 0.010 | 0.012 | |
SAW | 0.07 | 0.34 | 1.24 | 1.02 | 0.05 | 0.25 | – | 0.013 | 0.015 | |
F500W, 35 mm | MIG/MAG | 0.05 | 0.44 | 1.5 | 1.43 | – | – | – | 0.011 | 0.016 |
SAW | 0.07 | 0.20 | 1.02 | 1.08 | – | – | – | 0.014 | 0.015 | |