Fig. 14From: The environment-induced cracking of as-annealed Ni3(Si,Ti) and Ni3(Si,Ti) with 2Mo in sodium chloride solutionsThe representative fracture appearances of a as-annealed Ni3(Si,Ti) at 1000Â MPa and b as-annealed Ni3(S,Ti) with 2Mo at 1450Â MPa in 0.5Â kmol/m3 NaCl solution at 313Â K ( in the EIC-dominated region)Back to article page